| Thermo-Tork - for use up to 400°C (750°F) |
| Products |
Characteristics and Uses |
Density
g/cm³
(45 lbs./cu.ft.)
(min.) |
ASTM F 36
Compressibility
% @ 34.5 MPa
(5000 psi) |
Minimum
Recovery
% |
ASTM F 152
Tensile
Strength
(MPa) psi |
ASTM F 36 Oil No. 3 |
ASTM F 36 Fuel B |
Composition |
Tensile
Loss
Maximum % |
Thickness
Increase
Maximum % |
Compressibility
%
Maximum |
Weight
Increase
Maximum % |
Thickness
Increase
Maximum % |
Fiber |
Rubber
Binder |
| TN-9045 |
An economical. heavy-duty material for service in elevated temperature applications. Unique Latent Cure, binder system adds additional temperature resistance over conventional binders. For applications up to 400°C (750°F). |
1.28 (80) |
15-25 |
45 |
10.3 (1500) |
55 |
20 |
30 |
30 |
15 |
Acrylic/Blend |
Latent Cure System
Acrylic |
| TN-9014 |
Economical compressed material with a Fully Cured nitrile binder. Excellent fuel and oil resistance with a blend of cellulose and aramid fibers. For applications up to 290°C (550°F). |
1.44 (90) |
7-20 |
45 |
17.2 (2500) |
45 |
20 |
30 |
25 |
20 |
Aramid/Cellulose |
Fully Cured
Nitrile Butadiene |
| TN-9015 |
Economical material with a Latent Cure nitrile binder. Conforms well to flange surface imperfections. Blend of cellulose and aramid fibers. Excellent fuel and oil resistance. For applications up to 290°C (550°F). |
1.28 (80) |
12-27 |
30 |
10.3 (1500) |
50 |
25 |
- |
35 |
25 |
Aramid/Cellulose |
Latent Cure System
Nitrile Butadiene |
| TS-9016 |
Economical compressed material with a Fully Cured styrene binder. Recommended for oil and water applications. Contains a blend of cellulose and aramid fibers. For applications up to 290°C (550°F). |
1.44 (90) |
10-25 |
40 |
12.4 (1800) |
- |
25-65 |
- |
- |
10-40 |
Aramid/Cellulose |
Fully Cured
Styrene Butadiene |
| TS-9013 |
Economical Controlled-Swell material. Conforms well to flange surface imperfections. This material contains a latent cure styrene binder with a blend of cellulose and aramid fibers. Recommended for water and oil applications up to 290°C (550°F). |
1.36 (85) |
12-25 |
25 |
8.3 (1200) |
- |
30-70 |
- |
- |
20-50 |
Aramid |
Latent Cure System
Styrene Butadiene
"Controlled Swell" |