| Synthseal® – for use up to 180°C (350°F) |
| Products |
Characteristics and Uses |
Density
g/cm³
(45 lbs./cu.ft.)
(min.) |
ASTM F 36
Compressibility
% @ 34.5 MPa
(5000 psi) |
Minimum
Recovery
% |
ASTM F 152
Tensile
Strength
(MPa) psi |
ASTM F 36 Oil No. 3 |
ASTM F 36 Fuel B |
Composition |
Tensile
Loss
Maximum % |
Thickness
Increase
Maximum % |
Compressibility
%
Maximum |
Weight
Increase
Maximum % |
Thickness
Increase
Maximum % |
Fiber |
Rubber
Binder |
| D-8080 |
D-8080 is a non-asbestos formulated gasket material designed as a direct substitute for compressed asbestos and asbestos-containing beater addition products. It is designed for low-to-moderate flange pressures at temperatures above 180°C (350°F) and is suitable for dry heat applications, electrical fixtures, and other light duty appliances. It can also be used as a radiant heat shield in applications where some degree of insulation is needed. |
|
|
|
|
|
|
|
|
|
|
|
| N-8092 |
Excellent crush resistance at high flange pressures. Nitrile binder. Recommended for sealing oil, fuels, and water up to 180°C (350°F). |
1.20 (75) |
15-30 |
35 |
11.0 (1600) |
30 |
20 |
40 |
40 |
20 |
Reinforced Cellulose |
Nitrile Butadiene |
| N-8094 |
An economical material exhibiting very good crush resistance at high flange pressures. Recommended for sealing oils, fuels, and water up to 180°C (350°F). Fully Cured nitrile binder. |
.87 (54) |
28-42 |
20 |
8.6 (1250) |
30 |
7 |
45 |
50 |
7 |
Reinforced Cellulose |
Fully Cured
Nitrile Butadiene |
| N-8090 |
A reinforced fiber and Latent Cured nitrile binder composition with outstanding sealing characteristics. Excellent oil resistance. For applications up to 180°C (350°F). |
1.28 (80) |
15-25 |
35 |
13.8 (2000) |
45 |
30 |
50 |
30 |
20 |
Reinforced Cellulose |
Latent Cure System
Nitrile Butadiene |
| S-8091 |
Seals oils, fuels, and low-pressure steam. Controlled-Swell with latent cure styrene binder. For applications up to 180°C (350°F). |
1.20 (75) |
15-25 |
25 |
12.4 (1800) |
– |
30-75 |
– |
– |
25-50 |
Reinforced Cellulose |
Latent Cure System
Styrene Butadiene
“Controlled-Swell” |